Property
|
Basalt
|
E-glass
|
Asbestos
|
Silica
|
Ceramic
|
Stainless steel
|
Carbon
|
Aramid
|
Thermal limit of application [[°C]
|
-260...+850
|
-60...+460
|
+500
|
+1050
|
+1200
|
+600
|
+2000
|
+250
|
Vitrification temperature [°C]
|
1050
|
600
|
450...700
|
1300...1670
|
-
|
-
|
-
|
280...300
|
Melting temperature [°C]
|
1450
|
1120
|
1500
|
2000
|
176
|
1400...1600
|
2500
|
370...500
|
Glow loss [%]
|
1.91
|
0.32
|
13.5
|
-
|
-
|
-
|
-
|
-
|
Thermal conductivity [W/m.K]
|
1.1...1.6
|
0.85...1.3
|
-
|
1.4
|
0.23
|
20...100
|
5...185
|
0.04...0.13
|
Specific heat capacity [KJ/kg.K]
|
0.86
|
0.84
|
1.05...1.1
|
0.96
|
1.1
|
0.51
|
0.71
|
1.2...1.4
|
Linear expansion coeff. [x10-7/K]
|
5.5
|
5
|
-
|
0.5
|
-
|
0.16
|
-0.1...-1.3
|
-0.35
|
Density [kg/dm3]
|
2.60...2.80
|
2.52...2.63
|
2.00...2.6
|
2.00...2.73
|
2.55
|
7.90
|
1.67... 2.15
|
|
E-modulus [GPa]
|
91 ... 110
|
73
|
30 ... 190
|
60 ... 72
|
110 ... 125
|
176 ... 196
|
160 ... 830
|
|
Absorption of humidity (65%RH) [%]
|
< 0.1
|
< 0.1
|
1.6 ... 1.9
|
0
|
0.1
|
0
|
0.01
|
N
|
Parameter
|
Unit
|
RB-10-600
|
RB-12-600
|
RB-15-600
|
1
|
Dia. of elementary fiber
|
m
|
10.0±2
|
12.0±2
|
15.0±2
|
2
|
Tensile strenght
|
mN/tex
|
600.0±20
|
580.0±20
|
530.0±20
|
3
|
Mass share of substance removed by heating (at least)
|
%
|
0.8
|
0.8
|
0.8
|
4
|
Mass share of moisture no more than
|
%
|
5.0
|
5.0
|
5.0
|
5
|
Temperature range of exploitation
|
[°C]
|
(-267)...(+850)
|
||
N
|
Parameter
|
Unit
|
RB-10-1200
|
RB-12-1200
|
RB-15-1200
|
1
|
Dia. of elementary fiber
|
m
|
10.0±2
|
12.0±2
|
15.0±2
|
2
|
Tensile strenght
|
mN/tex
|
560.0±20
|
520.0±20
|
500.0±20
|
3
|
Mass share of substance removed by heating (at least)
|
%
|
0.8
|
0.8
|
0.8
|
4
|
Mass share of moisture no more than
|
%
|
5.0
|
5.0
|
5.0
|
5
|
Temperature range of exploitation
|
[°C]
|
(-267) ... (+850)
|
||